Lagging Performance Specifications

COLD VULCANISED RUBBER LAGGING

COLD VULCANISED RUBBER LAGGING – NATURAL

Rubber lagging manufactured using an abrasion resistant top rubber layer and a buffed CN bonding layer to provide high levels of adhesion.

RUBBER PROPERTIES

Base Polymer Blend
Hardness Range 65+/-5 ASTM D2240
Tensile Strength >18 Mpa ASTM D412
Elongation at Break >550% ASTM D412
Abrasion Loss (Volume Loss) <70mm3 DIN 53516 – non rotating – method A

ADHESION REQUIREMENTS

Adhesion to steel @ +25 C >12N/mm ASTM D429 method B 90 deg peel test
Adhesion to steel @ -40 C >15N/mm ASTM D429 method B 90 deg peel test
Adhesion to steel @ +50 C >9N/mm ASTM D429 method B 90 deg peel test

DIMENSIONS

PRODUCT DESCRIPTION PRODUCT CODE WIDTH THICKNESS STANDARD ROLL LENGTH WEIGHT/lm
Rubber lagging 10mm ELA-RL-DIA-N-10 249mm-251mm 10mm-11mm 80m 2.78kg
Rubber lagging 12mm ELA-RL-DIA-N-12 249mm-251mm 12mm-13mm 65m 3.93kg
Rubber lagging 15mm ELA-RL-DIA-N-15 249mm-251mm 15mm-16mm 50m 4.30kg
Rubber lagging 20mm ELA-RL-DIA-N-20 249mm-251mm 19mm-20mm 40m 5.70kg
Rubber lagging 25mm ELA-RL-DIA-N-25 249mm-251mm 24mm-25mm 30m 7.10kg

Product code for different lengths: Add 5 digit number indicating length in mm.

Example: 12 mm 65m roll product code: ELA-RL-DIA-N-12-65000
15 mm 1.2m strip product code: ELA-RL-DIA-N-15-01200

For strips always allow 100 mm extra length over the pulley face width to have 50 mm at each end of overhang.

Thickness variation (all strips/pulley) +/-0.5mm

Rubber lagging with thickness > 15mm only recommended for pulleys with diameters over 400mm.