Lagging Performance Specifications
Hot Vulcanised Ceramic Lagging
Hot Vulcanised Ceramic Lagging – FRAS
Hot vulcanising ceramic lagging is manufactured using high abrasion resistant ceramic tiles vulcanised to an abrasion resistant top rubber layer, a buffed CN bonding layer to provide high levels of adhesion and an uncured bonding layer to provide high levels of adhesion after autoclave curing.This ceramic lagging is for use in applications where there is a risk of fire and/or explosion such as underground coal mines, and grain and sugar handling facilities and is a safety critical item.
RUBBER PROPERTIES
Base Polymer | Blend | |
Hardness Range | 65+/-5 | ASTM D2240 |
Tensile Strength | >16 Mpa | ASTM D412 |
Elongation at Break | > 500% | ASTM D412 |
Abrasion Loss (Volume Loss) | <150mm3 | DIN 53516 – non rotating – method A |
FRAS | PASS | MDG 3608 |
CERAMIC PROPERTIES
Aluminium oxide tile | >96% Alumina |
Specific gravity | >3.4 |
Vickers hardness | >1100 |
Flex crack resistance (MPa*m1/2) | >4.0 |
Micro particle size range | 1-8 |
ADHESION REQUIREMENTS
Adhesion to steel @ +25 C | >20N/mm & 100% Rubber tear | ASTM D429 method B |
Adhesion to steel @ -40 C | >20N/mm & 100% Rubber tear | ASTM D429 method B |
Adhesion to steel @ +50 C | >20N/mm & 100% Rubber tear | ASTM D429 method B |
DIMENSIONS
DIMPLE TILES
PRODUCT DESCRIPTION | PRODUCT CODE | WIDTH | THICKNESS | STANDARD ROLL LENGTH | WEIGHT/lm |
Ceramic lagging 12mm | ELA-SRC-F-12KV | 251mm-255mm | 13mm-14.2mm | 9.7m | 5.19kg |
Ceramic lagging 15mm | ELA-SRC-F-15KV | 251mm-255mm | 16mm-17.2mm | 9.7m | 5.49kg |
Ceramic lagging 20mm | ELA-SRC-F-20KV | 251mm-255mm | 21mm-22.2mm | 9.7m | 6.29kg |
Ceramic lagging 25mm | ELA-SRC-F-25KV | 251mm-255mm | 26mm-27.2mm | 9.7m | 7.09kg |
PLAIN TILES
PRODUCT DESCRIPTION | PRODUCT CODE | WIDTH | THICKNESS | STANDARD ROLL LENGTH | WEIGHT/lm |
Ceramic lagging 12mm | ELA-SRC-F-12PV | 251mm-255mm | 13mm-14.2mm | 9.7m | 5.39kg |
Ceramic lagging 15mm | ELA-SRC-F-15PV | 251mm-255mm | 16mm-17.2mm | 9.7m | 6.69kg |
Ceramic lagging 20mm | ELA-SRC-F-20PV | 251mm-255mm | 21mm-22.2mm | 9.7m | 6.49kg |
Ceramic lagging 25mm | ELA-SRC-F-25PV | 251mm-255mm | 26mm-27.2mm | 9.7m | 7.29kg |
Thickness variation (all strips/pulley) +/-0.5 mm
END PIECES
PRODUCT DESCRIPTION | PRODUCT CODE | WIDTH | THICKNESS | STANDARD LENGTH | WEIGHT/lm |
End piece 12mm | ELA-SR-END-F-12V | 251mm-255mm | 13mm-14.2mm | 130mm | 0.50kg |
End piece 15mm | ELA-SR-END-F-15V | 251mm-255mm | 16mm-17.2mm | 130mm | 0.60kg |
End piece 20mm | ELA-SR-END-F-20V | 251mm-255mm | 21mm-22.2mm | 130mm | 0.66kg |
End piece 25mm | ELA-SR-END-F-25V | 251mm-255mm | 26mm-27.2mm | 130mm | 0.71kg |
Product code for different lengths: Add 5 digit number indicating length in mm.
Example:
Roll: | 12 mm 9.7 m roll product code: |
ELA-SRC-F-12KV-09700 | |
Strip: | 15 mm 1.2m ceramic length strip product code: |
ELA-SRC-F-15KV-01200 | |
Ceramic strips are supplied with 130mm rubber end pieces on each end. |
Ceramic lagging with thickness > 15 mm only recommended for pulleys with diameters over 600mm.