Lagging Performance Specifications
POLYURETHANE LAGGING
HOT VULCANISED POLYURETHANE LAGGING
Polyurethane lagging manufactured using abrasion resistant TPU inserts and an uncured bonding layer to provide high levels of adhesion after autoclave curing.
RUBBER
Base Polymer |
Natural and synthetic rubber |
|
Hardness Range | 65+/-5 | ASTM D2240 |
Tensile Strength | >18 MPa | ASTM D412 |
Elongation at Break | >550% | ASTM D412 |
Abrasion Loss (Volume Loss) | <70mm3 | DIN 53516 – non rotating – method A |
ADHESION REQUIREMENTS
Adhesion to steel @ +25 C | >20N/mm | ASTM D429 method B | 90 deg peel test |
Adhesion to steel @ -40 C | >30N/mm | ASTM D429 method B | 90 deg peel test |
Adhesion to steel @ +50 C | >10N/mm | ASTM D429 method B | 90 deg peel test |
POLYURETHANE PROPERTIES
Hardness (shore A) | 85+/-5 | ASTM D2240 |
Tensile strength | >14 MPa | ASTM D412 |
Elongation at Break | >500% | ASTM D412 |
Abrasion Loss (Volume Loss) | <35mm | DIN 53516 – non rotating – method A |
DIMENSIONS
PRODUCT DESCRIPTION | PRODUCT CODE | WIDTH | THICKNESS | STANDARD ROLL LENGTH | WEIGHT/lm |
Polyurethane lagging 12mm | ELA-PU-PLN-N-12V | 249mm-251mm | 12.2mm-13.2mm | 9.7m | 4.21kg |
Polyurethane lagging 20mm | ELA-PU-PLN-N-20V | 249mm-251mm | 20.2mm-21.2mm | 9.7m | 6.90kg |
Product code for different lengths: Add 5 digit number indicating length in mm.
Example: | 12 mm 9.7m roll product code: ELA-PU-PLN-N-12V-09700 |
20 mm 1.2m strip product code: ELA-PU-PLN-N-20V-01200 |
For strips always allow 100 mm extra length over the pulley face width to have 50 mm at each end of overhang.
Thickness variation (all strips/pulley) +/-0.5mm
Polyurethane lagging with thickness > 15mm only recommended for pulleys with diameters over 400mm.